Stanyl® HFX31SW WT94001

About
Stanyl®是我们的高性能聚酰胺46，可应用于汽车、电子电气、齿轮、和户外动力设备。&&Stanyl®作为高性能聚酰胺，在对耐热性、设计硬度、摩擦磨耗以及流动性都有要求的严苛的应用中表现无与伦比。&&Stanyl®能在高达220°C时依旧保持良好的机械性能，这使它比PPA、PA6T、PA9T、PPS 和LCP更适合超高性能应用.

About

Stanyl®是我们的高性能聚酰胺46，可应用于汽车、电子电气、齿轮、和户外动力设备。&&Stanyl®作为高性能聚酰胺，在对耐热性、设计硬度、摩擦磨耗以及流动性都有要求的严苛的应用中表现无与伦比。&&Stanyl®能在高达220°C时依旧保持良好的机械性能，这使它比PPA、PA6T、PA9T、PPS 和LCP更适合超高性能应用.

Product Description
Supplier	DSM
Generic	PA 46
Material Status	Commercial: Active
Features	High liquidity,Halogen free,Glass fiber reinforced

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	8350 / –	MPa	ISO 527-1-2
Fracture stress	90 / –	MPa	ISO 527-1/-2
Tensile strain
fracture	1.8 / –	%	ISO 527-1/2
Bending modulus	8200 / –	MPa	ISO 178
bending strength	115 / –	MPa	ISO 178

THERMAL	Nominal value	Unit	Test method
Melting temperature
10℃ / min	295 / *	℃	ISO 11357-1/-3
Glass transition temperature
10℃/min	75 / *	°C	ISO 11357-1/-2
Hot deformation temperature
1.8 MPa	285 / *	℃	ISO 75-1/2
Combustibility (1.5mm thickness)	V-0 / *	class	IEC 60695-11-10
Test thickness	1.6 / *	mm	IEC 60695-11-10
Combustibility at a thickness of h	V-0 / *	class	IEC 60695-11-10
The thickness of the test specimen used for testing	0.2 / *	mm	IEC 60695-11-10

Other performance	Nominal value	Unit	Test method
Water absorption rate
23 ℃, 24 hours, in water	1.5 / *	%	ISO 62
Moisture absorption rate	1.9 / *	%	Sim. to ISO 62

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	3 / –	kJ/m²	ISO 179/1eA

PHYSICAL	Nominal value	Unit	Test method
Density	1.51	g/cm³	ISO 1183

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.