| About |
|---|
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Halogen free,Heat Resistance, Good,High liquidity,Heat Stabilized |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1360 | kg/m³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.4 / * | % | ISO 294-4 |
| Shrinkage rate | |||
| MD | 1.5 / * | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7700 / – | MPa | ISO 527-1-2 |
| Fracture stress | 115 / – | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | 2.7 / – | % | ISO 527-1/2 |
| Bending modulus | 7000 / – | MPa | ISO 178 |
| bending strength | 170 / – | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 295 / * | ℃ | ISO 11357-1/-3 |
| Glass transition temperature | |||
| 10℃/min | 75 / * | °C | ISO 11357-1/-2 |
| Hot deformation temperature | |||
| 1.8 MPa | 276 / * | ℃ | ISO 75-1/2 |
| Hot deformation temperature | |||
| 0.45 MPa | 284 / * | ℃ | ISO 75-1/2 |
| Combustibility (1.5mm thickness) | V-0 / * | class | IEC 60695-11-10 |
| Test thickness | 3 / * | mm | IEC 60695-11-10 |
| UL certification | Yes / * | – | – |
| Combustibility at a thickness of h | V-0 / * | class | IEC 60695-11-10 |
| The thickness of the test specimen used for testing | 0.4 / * | mm | IEC 60695-11-10 |
| UL certification | Yes / * | – | – |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 1 GHz | 3.5 / – | IEC 60250 | |
| Dissipation factor | |||
| 1 GHz | 100 / – | E-4 | IEC 60250 |
| Dielectric strength | 30 / – | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 500 / – | V | IEC 60112 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.5 / – | kJ/m² | ISO 179/1eA |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | null |
| Drying time | 4.0 to 8.0 | hr | null |
| Temperature at the rear of the barrel | 280 to 320 | °C | null |
| Temperature in the middle of the barrel | 300 to 320 | °C | null |
| Front temperature of material barrel | 300 to 320 | °C | null |
| Nozzle temperature | 300 to 320 | °C | null |
| Processing (melt) temperature | 310 to 320 | °C | null |
| Mold temperature | 80 to 120 | °C | null |
| Injection speed | Moderate-Fast | null | |
| Back pressure | 2.00 to 10.0 | MPa | null |
| Screw compression ratio | 2.5:1.0 | null | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |