| About |
|---|
| 20% Glass Reinforced, High Flow, Halogen free and free of red phosphorous&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Good liquidity,Flame Characteristics,Low to no phosphorus content |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 1.5 | % | |
| MD | 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7400 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.7 | % | ISO 527-2 |
| Bending modulus | 7000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 75.0 | ℃ | ISO 11357-2 |
| Melting temperature | 295 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 30 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1.00 GHz | 3.50 | IEC 60250 | |
| Compared to the leakage tracing index | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.40 mm | V-0 | ||
| 3.0 mm | V-0 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 280 to 320 | °C | |
| Barrel middle temperature | 300 to 320 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 300 to 320 | °C | |
| Processing (melt) temperature | 305 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 0.500 to 3.00 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |