| About |
|---|
| 35% Glass Reinforced, High Flow, Halogen free and free of red phosphorous&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Halogen free,High liquidity,Low to no phosphorus content |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Molding Shrinkage | |||
| parallel | 0.4 | % | ISO 294-4 |
| normal | 1.1 | % | ISO 294-4 |
| Water Absorption | 2 | % | ISO 62 |
| Density | 1510 | kg/m³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| 11800 | MPa | ISO 527 | |
| 120℃ | 6400 | MPa | ISO 527 |
| 160℃ | 5700 | MPa | ISO 527 |
| Tensile Strength | |||
| brk | 140 | MPa | ISO 527-2 |
| brk，120℃ | 83 | MPa | ISO 527-2 |
| brk，160℃ | 70 | MPa | ISO 527-2 |
| Tensile Strain | |||
| brk | 2.4 | % | ISO 527 |
| brk，120℃ | 4 | % | ISO 527 |
| brk，160℃ | 4.4 | % | ISO 527 |
| Flexural Modulus | |||
| 10500 | MPa | ISO 178 | |
| 120℃ | 6900 | MPa | ISO 178 |
| 160℃ | 6300 | MPa | ISO 178 |
| Flexural Strength | |||
| 210 | MPa | ISO 178 | |
| 120℃ | 135 | MPa | ISO 178 |
| 160℃ | 115 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotched Impact strength | 50 | kJ/m² | ISO 179/1eU |
| Charpy notched Impact strength | 9 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 295 | ℃ | ISO 11357-3 |
| HDT | |||
| 1.80 MPa | 285 | ℃ | ISO 75-1/-2 |
| Coeff.of linear therm expansion | |||
| parallel | 0.17 | ×10-4/℃ | ISO 11359-2 |
| normal | 0.7 | ×10-4/℃ | ISO 11359-2 |
| parallel | 0.3 | ×10-4/℃ | ASTM D696 |
| normal | 0.4 | ×10-4/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 | |
| Relative Temperature Index | |||
| elec，0.18 mm | 120 | ℃ | UL-746B |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistivity | >1E13 | ohm·m | IEC 62631-3-1 |
| Electric strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Relative Permittivity | |||
| 100Hz | 4.4 | IEC 62631-2-1 | |
| 1MHz | 4.1 | IEC 62631-2-1 | |
| 1GHz | 3.9 | IEC 62631-2-1 | |
| 10GHz | 3.8 | IEC 62631-2-1 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Injection speed | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 300 to 310 | °C | |
| Barrel middle temperature | 305 to 315 | °C | |
| Barrel front temperature | 310 to 320 | °C | |
| Nozzle temperature | 315 to 325 | °C | |
| Processing (melt) temperature | 320 to 330 | °C | |
| Mold temperature | 100 to 120 | °C | |
| Back pressure | 0.500 to 3.00 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |