| About |
|---|
| 30% Glass Reinforced, Heat Stabilized&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.3 | % | ISO 294-4 |
| MD | 0.50 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.6 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| — | 10000 | MPa | ISO 527-2 |
| 120℃ | 5500 | MPa | ISO 527-2 |
| 160℃ | 5000 | MPa | ISO 527-2 |
| 180℃ | 4400 | MPa | ISO 527-2 |
| 200℃ | 4000 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| fracture | 210 | MPa | ISO 527-2 |
| Fracture, 120 ℃ | 110 | MPa | ISO 527-2 |
| Fracture, 160 ℃ | 100 | MPa | ISO 527-2 |
| Fracture, 180 ℃ | 95.0 | MPa | ISO 527-2 |
| Fracture, 200 ℃ | 90.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| fracture | 4.0 | % | ISO 527-2 |
| Fracture, 120 ℃ | 7.5 | % | ISO 527-2 |
| Fracture, 160 ℃ | 7.5 | % | ISO 527-2 |
| Fracture, 180 ℃ | 7.5 | % | ISO 527-2 |
| Fracture, 200 ℃ | 7.5 | % | ISO 527-2 |
| Bending modulus | ISO 178 | ||
| — | 9000 | MPa | ISO 178 |
| 120℃ | 4700 | MPa | ISO 178 |
| 160℃ | 3900 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 11 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 65 | kJ/m² | ISO 179/1eU |
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 11 | kJ/m² | ISO 180-1A |
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 290 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 290 | ℃ | ISO 75-2/B |
| Melting temperature | 295 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 6.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.5E-5 | 1/℃ | ISO 11359-2 |
| Temperature index | |||
| 5000 hr | 159 | ℃ | IEC 60216 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 4.40 | IEC 60250 | |
| 1 MHz | 4.00 | IEC 60250 | |
| 1.00 GHz | 3.60 | IEC 60250 | |
| Compared to the leakage tracing index | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.9 mm | HB | IEC 60695-11-10, -20 | |
| 1.6 mm | HB | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 280 to 320 | °C | |
| Barrel middle temperature | 300 to 320 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 300 to 320 | °C | |
| Processing (melt) temperature | 305 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 2.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |