| About |
|---|
| Unreinforced, Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1430 | kg/m³ | ISO 1183 |
| Moisture Absorption | 2.35 | % | Sim. to ISO 62 |
| Mold Shrinkage | |||
| Parallel | 1.5 | % | Sim. to ISO 294-4 |
| Vertical normal | 1.5 | % | Sim. to ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-1/-2 |
| Tensile Stress | |||
| Yield yld | 80 | MPa | ISO 527-1/-2 |
| Tensile Strain | |||
| Broken BRK | 7 | % | ISO 527-1/-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Strength | 130 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23°C | 4 | KJ/m² | ISO 179/1A |
| -30°C | 3 | KJ/m² | ISO 179/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10°C/min | 295 | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature HDT | |||
| Unannealed, 1.80MPa | 190 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel | 8 | ×10-5/℃ | ISO 11357-1/-2 |
| Vertical normal | 9 | ×10-5/℃ | ISO 11357-1/-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5mm | V-0 | calss | IEC 60695-11-10 |
| 3.0mm | V-0 | calss | IEC 60695-11-10 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E+13 | ohm·m | IEC 62631-3-1 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Compared Tracking Index | 225 | V | IEC 60112 |
| Dielectric Constant | |||
| 100 Hz | 3.8 | IEC 62631-2-1 | |
| 1 MHz | 3.5 | IEC 62631-2-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |