| Staramide B28N is a Nucleated and Unreinforcred Polyamide 6 Injection Molding Resin&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Nucleation,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 1.1 to 1.5 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 10 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.6 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | > 100 | kJ/m² | ISO 179/1eU |
| 23℃ | > 270 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 3.0 | kJ/m² | ISO 180-1A |
| -20℃ | 4.0 | kJ/m² | ISO 180-1A |
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 180 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 60.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B50 | 210 | ℃ | ISO 306 |
| B120 | 200 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.29 | W/m/K | ISO 8302 |
| Relative temperature index | 65.0 | ℃ | UL 746 |
| Electrical performance | 65.0 | ℃ | UL 746 |
| Impact mechanical performance | 65.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 16 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 5.8E-3 | IEC 60250 | |
| 60 Hz | 5.8E-3 | IEC 60250 | |
| 1 MHz | 0.018 | IEC 60250 | |
| Compared to the leakage tracing index | IEC 60112 | ||
| CTI | 600 | V | IEC 60112 |
| Solution B | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Extreme oxygen index | 24 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| Tensile modulus | 2700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 70.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.5 | % | ASTM D638 |
| fracture | > 15 | % | ISO 527-2/50 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 85.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 240 to 250 | °C | |
| Barrel front temperature | 250 to 260 | °C | |
| Processing (melt) temperature | 250 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.079 in/min |
| 4. at Yield |
| 5. 120x10x4 mm |
| 6. ROA |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |