| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| lvory | 1.06 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 0.7 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 17.2 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 3.0 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 24hr | 0.3 | % | ASTM D570 |
| Shrinkage rate | 0.5 | % | ASTM D955 |
| Specular luster | 96 | % | ASTM D523 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 130 | J/m | ASTM D256 |
| 23℃，6.4mm | 170 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 92 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 104 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50-6.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 5 mm/min | 50 | MPa | ASTM D638 |
| Tensile strain | |||
| 5 mm/min | 32 | % | ASTM D638 |
| Bending modulus | |||
| 2.80 mm/min | 2500 | MPa | ASTM D790 |
| bending strength | |||
| 2.80 mm/min | 73 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 108 | ASTM D785 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |