| About |
|---|
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | ABS transparent |
| Material Status | Commercial: Negative |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D-792 |
| Mold shrinkage rate | |||
| parallel | 0.4-0.8 | % | ASTM D-955 |
| vertical | 0.4-0.8 | % | ASTM D-955 |
| Melt index | 22 | g/10min | ASTM D-1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，1/4 inch | 14 | kJ/m² | ISO 179/1eA |
| 23℃，1/8 inch | 15 | KJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 18.56Mpa, unannealed, 6.4 mm | 81 | ℃ | ASTM D-648 |
| Vicat Softening Temp | |||
| B/50 | 93 | ℃ | ISO R-306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5-3.0 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3.2mm | 90 | % | ASTM D-1003 |
| Haze | |||
| 3.2mm | 2 | % | ASTM D-1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ASTM D-638 |
| tensile strength | |||
| fracture | 370 | MPa | ASTM D-638 |
| yield | 400 | MPa | ASTM D-638 |
| Tensile strain | |||
| Fracture, 5mm/min | 25 | % | ASTM D-638 |
| Bending modulus, 2.8mm/min | 19000 | MPa | ASTM D-790 |
| Bending strength, 2.8mm/min | 550 | MPa | ASTM D-790 |
| Rockwell hardness | |||
| R-level | 110 | ASTM D-785 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |