| About |
|---|
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Forming shrinkage rate | |||
| TD : 23°C, 2.00 mm | 1.4 | % | ISO 294-4 |
| MD : 23°C, 2.00 mm | 1.2 | % | ISO 294-4 |
| Water absorption rate | |||
| 23°C, 24 hr | 0.8 | % | ISO 62 |
| Saturation, 23 ° C, 50% RH | 2.3 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23°C | 3200.0 | MPa | ISO 527-2 |
| Tensile stress | |||
| Yield, 23 ° C | 75.2 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ° C | 3.5 | % | ISO 527-2 |
| Fracture, 23 ° C | 22 | % | ISO 527-2 |
| Bending modulus | |||
| 23°C | 3199.2 | MPa | ISO 178 |
| bending strength | |||
| 23°C | 91.7 | mpa | ISO 178 |
| Poisson’s ratio | – | ||
| 23°C | 0.4 | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| +23°C | 2.38 | ftlb/in² | ISO 179/1eA |
| -30°C | 1.9 | ftlb/in² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| +23°C | N | ftlb/in² | ISO 179/1eU |
| -30°C | N | ftlb/in² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| +23°C | 2.38 | ftlb/in² | ISO 180/1A |
| -30°C | 2.38 | ftlb/in² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.80 MPa, unannealed | 65 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 225 | ℃ | ISO 75-2/B |
| Melting temperature | 244 | ℃ | ISO 11357-3 |
| CLTE | |||
| Flow : 23 to 55°C, 2.00 mm | 110 | E-6/K | ISO 11359-2 |
| Transverse : 23 to 55°C, 2.00 mm | 110 | E-6/K | ISO 11359-2 |
| RTI Elec | |||
| 0.400 mm | 130 | ℃ | UL 746 |
| 0.750 mm | 130 | ℃ | UL 746 |
| 1.50 mm | 130 | ℃ | UL 746 |
| 3.00 mm | 130 | ℃ | UL 746 |
| RTI Imp | |||
| 0.400 mm | 65 | ℃ | UL 746 |
| 0.750 mm | 65 | ℃ | UL 746 |
| 1.50mm | 85 | ℃ | UL 746 |
| 3.00 mm | 85 | ℃ | UL 746 |
| RTI Str | |||
| 0.400 mm | 100 | ℃ | UL 746 |
| 0.750 mm | 100 | ℃ | UL 746 |
| 1.50 mm | 100 | ℃ | UL 746 |
| 3.00 mm | 110 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 1.00 mm | 1E9 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.00 mm | 330 | kV/in | IEC 60243 |
| Arc resistance | – | ||
| 3.00 mm | 5 | ASTM D 495 | |
| Compared to the leakage tracing index | |||
| 3.00 mm | 600 | V | IEC 60112 |
| High current arc ignition (HAI) | |||
| 0.400 mm | PLC0 | – | UL 746 |
| 0.750 mm | PLC0 | – | UL 746 |
| 1.50 mm | PLC0 | – | UL 746 |
| 3.00 mm | PLC0 | – | UL 746 |
| High Voltage Arc Tracing Rate (HVTR) | – | ||
| 3.00 mm | PLC1 | UL 746 | |
| Hot wire ignition (HWI) | |||
| 0.400 mm | PLC4 | – | UL 746 |
| 0.750 mm | PLC4 | – | UL 746 |
| 1.50 mm | PLC4 | – | UL 746 |
| 3.00 mm | PLC3 | – | UL 746 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | ℃ | |
| Drying time | 4 | h | |
| Rear section barrel temperature | 240-270 | ℃ | |
| Middle section barrel temperature | 240-270 | ℃ | |
| Front section barrel temperature | 240-270 | ℃ | |
| Nozzle temperature | 240-270 | ℃ | |
| Processing (melt) temperature | 250-270 | ℃ | |
| Mold temperature | 65-95 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |