| About |
|---|
| Starflam PA66 30V Z32 is a Halogen Free and Red Phosphorous Free Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as PA6630VZ32)&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | V-0,Low to no phosphorus content,Halogen free,Flame Characteristics |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：4.0 mm | 0.20 to 0.40 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 119 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.6 | % | ISO 527-2 |
| Bending modulus | 9200 | MPa | ISO 178 |
| bending strength | 175 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 32 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 233 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 450 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm, E2P measurement | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 265 to 275 | °C | |
| Barrel middle temperature | 270 to 280 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Processing (melt) temperature | 270 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Break |
| 4. 80x10x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |