| About |
|---|
| Starflam PZ0042E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced Polyamide 6 Injection Molding Resin (also known as PF1004Z22 or PA620U9GFZ22)&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | V-2,Low to no phosphorus content,Halogen free,Flame Characteristics |
| Availabilitys | Europe,Africa & Middle East ,Asia Pacific,Latin America,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.70 to 0.90 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 95.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.2 | % | ISO 527-2 |
| Bending modulus | 6150 | MPa | ISO 178 |
| bending strength | 160 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 45 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 100 mm span | 185 | ℃ | ISO 75-2/Ae |
| Relative temperature index | |||
| Electrical performance | 125 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-2 | UL 94 | |
| Glowing wire flammability index | |||
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 240 to 250 | °C | |
| Barrel middle temperature | 250 to 260 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 120x10x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |