| About |
|---|
| Starflam RF0057E is a Halogen Free and Red Phosphorous Free Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as RF1005Z270)&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Low to no phosphorus content,5VA,V-0 |
| Availabilitys | North America,Latin America,Africa & Middle East ,Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 1.0 to 1.2 | % | ISO 294-4 |
| MD：24 hrs | 0.15 to 0.25 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.20 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.6 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 130 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.4 | % | ISO 527-2/5 |
| Bending modulus | 8000 | MPa | ISO 178 |
| bending strength | 190 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 45 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 240 | ℃ | ISO 75-2/Af |
| Ball pressure test | |||
| 240℃ | 通过 | IEC 60695-10-2 | |
| Relative temperature index | 140 | ℃ | UL 746 |
| Electrical performance | 140 | ℃ | UL 746 |
| Impact mechanical performance | 110 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm in air | 16 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-0 | UL 94 | |
| 1.60 mm | 5VA | UL 94 | |
| Glowing wire flammability index | |||
| 0.40 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.4 mm | 775 | ℃ | IEC 60695-2-13 |
| 1 mm | 775 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 775 | ℃ | IEC 60695-2-13 |
| 3 mm | 825 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 265 to 275 | °C | |
| Barrel middle temperature | 270 to 280 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Processing (melt) temperature | 270 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Yield |
| 4. 80x10x4 mm |
| 5. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |