Starflam® RF0057E

About
Starflam RF0057E is a glass fiber reinforced, flame retardant PA66 for injection molded applications. The material is halogen free and red phosphorus free.

Product Description
Supplier	Ascend
Generic	PA6
Material Status	Commercial: Active

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.37	g/cm³	ISO 1183
Molding Shrinkage			ISO 294-4
Across Flow : 23°C, 2.00 mm	1.7	%	ISO 294-4
Flow : 23°C, 2.00 mm	1.0	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr	1.1	%	ISO 62
Equilibrium, 23°C, 50% RH	1.7	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile Modulus	9583.7	mpa	ISO 527-2
Tensile Strength	126.2	mpa	ISO 527-2
Tensile Strain	2.3	%	ISO 527-2
Flexural Modulus	9583.7	mpa	ISO 178
Flexural Strength	193.7	mpa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy notched Impact strength			ISO 179/1eA
+23°C	3.81	ftlb/in²	ISO 179/1eA
-30°C	3.81	ftlb/in²	ISO 179/1eA
-40°C	3.85	ftlb/in²	ISO 179/1eA
Charpy Unnotched Impact strength			ISO 179/1eU
+23°C	26.2	ftlb/in²	ISO 179/1eU
-30°C	27.6	ftlb/in²	ISO 179/1eU
-40°C	25.2	ftlb/in²	ISO 179/1eU
Izod Notched Impact strength			ISO 180/1A
+23°C	3.85	ftlb/in²	ISO 180/1A
-30°C	3.66	ftlb/in²	ISO 180/1A
-40°C	3.81	ftlb/in²	ISO 180/1A
Izod Unnotched Impact strength	21.4	ftlb/in²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
HDT			ISO 75-2/A
1.80 MPa, Unannealed	244	℃	ISO 75-2/A
0.45 MPa, Unannealed	260	℃	ISO 75-2/B
Melting temperature	262	℃	ISO 11357-3
Relative Temp Index(RTI)			UL 746
0.400 mm	65	℃	UL 746
0.800 mm	140	℃	UL 746
0.900 mm	140	℃	UL 746
1.50 mm	140	℃	UL 746
1.60 mm	140	℃	UL 746
2.00 mm	140	℃	UL 746
3.00 mm	140	℃	UL 746
Relative Temp Index(RTI)			UL 746
0.400 mm	65	℃	UL 746
0.800 mm	110	℃	UL 746
0.900 mm	110	℃	UL 746
1.50mm	110	℃	UL 746
1.60 mm	110	℃	UL 746
2.00 mm	110	℃	UL 746
3.00 mm	110	℃	UL 746
Relative Temp Index(RTI)			UL 746
0.400 mm	65	℃	UL 746
0.800 mm	140	℃	UL 746
0.900 mm	140	℃	UL 746
1.50 mm	140	℃	UL 746
1.60 mm	140	℃	UL 746
2.00 mm	140	℃	UL 746
3.00 mm	140	℃	UL 746

ELECTRICAL	Nominal value	Unit	Test method
Dielectric Strength	762	kV/in	IEC 60243
Comparative Tracking Index	600	V	IEC 60112
HAI			UL 746
0.400 mm	PLC0	–	UL 746
0.800 mm	PLC0	–	UL 746
0.900 mm	PLC0	–	UL 746
1.50 mm	PLC0	–	UL 746
1.60 mm	PLC0	–	UL 746
2.00 mm	PLC0	–	UL 746
3.00 mm	PLC0	–	UL 746
Hot Wire Ignition			UL 746
0.400 mm	PLC0	–	UL 746
0.800 mm	PLC0	–	UL 746
0.900 mm	PLC0	–	UL 746
1.50 mm	PLC0	–	UL 746
1.60 mm	PLC0	–	UL 746
2.00 mm	PLC0	–	UL 746
3.00 mm	PLC0	–	UL 746

Process Conditions
Injection Molding	Nominal value	Unit	Test method
Drying Temperature	80	℃
Drying Time	4	h
Maximum Moisture Content	0.15-0.25	%
Rear Temperature -Zone 1	265-275	℃
Middle Temperature -Zone 2	270-280	℃
Front Temperature -Zone 3	270-280	℃
Melt Temperature	270-280	℃
Mold Temperature	60-100	℃

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.