| About |
|---|
| Starflam RF0067K is a Halogen Free and Red Phosphorous Free Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding, CrossLinkable under Beta or Gamma Radiation. Data provided for material not crosslinled (0 kGy)&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | Flame Characteristics,V-0,Crosslinked radiation,Halogen free,Low to no phosphorus content |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.8 | % | ISO 527-2/5 |
| Bending modulus | 8200 | MPa | ISO 178 |
| bending strength | 141 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 30 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 197 | ℃ | ISO 75-2/Af |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 265 to 285 | °C | |
| Barrel front temperature | 280 to 290 | °C | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Back pressure | > 1.00 | MPa | |
| Screw speed | 80 to 120 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Break |
| 4. 80x10x4 mm |
| 5. Before Irradiation |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |