| About |
|---|
| Starglas OC004 is a 20 % Carbon Fiber Reinforced PPS Injection Molding Resin&& |
| Product Description | |
|---|---|
| Generic | PPS |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：4.0 mm | 0.15 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 16600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 144 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.1 | % | ISO 527-2/5 |
| Bending modulus | 15100 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| — | 193 | MPa | ISO 178 |
| — | 194 | MPa | ISO 178 |
| Fracture bending strain | 1.5 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 25 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 275 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64 mm span | 235 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 1.3E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 150 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 305 to 315 | °C | |
| Barrel middle temperature | 320 to 330 | °C | |
| Barrel front temperature | 330 to 345 | °C | |
| Processing (melt) temperature | 315 to 320 | °C | |
| Mold temperature | 140 to 165 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Yield |
| 4. at Break |
| 5. 2 mm/min |
| 6. 80x10x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |