| About |
|---|
| Starpylen M1000 is an Unfilled Polypropylene, Injection Molding Resin&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.0 mm | 1.5 – 2.0 | % | ISO 294-4 |
| Melt Flow Rate | |||
| 230℃，5.0kg | 6.0 – 12 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 35.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | >= 9.0 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 54.0 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 2600 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 165 | ℃ | ISO 3146 |
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 75.0 | ℃ | ISO 75-2/Af |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 9.00 | kJ/m² | ISO 179/1eU |
| Notched impact strength of cantilever beam | |||
| 23℃ | 14.0 | kJ/m² | ISO 180/1U |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70.0 | °C | |
| Drying time | 3.00 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 220-230 | °C | |
| Central temperature of the barrel | 220-230 | °C | |
| Barrel front temperature | 220-230 | °C | |
| Die temperature | 220-230 | °C | |
| Mold temperature | 30.0-50.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 120x10x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |