Stat-Tech™ AS-1000 AS Amber

About
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements.&&

About

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements.&&

Product Description
Supplier	Polyone
Generic	ABS
Material Status	Commercial: Active
Features	No shedding,Antistatic property
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	ASTM D792
Shrinkage rate
MD	0.40 to 0.60	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	35.0	MPa	ASTM D638
Bending modulus	20700	MPa	ASTM D790
bending strength	59.8	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, 3.2mm, injection molding	160	J/m	ASTM D256-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed, 6.35 mm	87.0	℃	ASTM D648
1.8 MPa, unannealed, 6.35 mm	74.0	℃	ASTM D648

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+9 to 1.0E+12	ohms	ASTM D257
Volume resistivity	1.0E+9 to 1.0E+12	ohms·cm	ASTM D257
Electrostatic attenuation
（Mil-B-81705C），12% RH，5000 kV to 50 kV	0.3	sec
（Mil-B-81705C），50% RH，5000 kV to 50 kV	0.1	sec

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	88	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.010 to 0.15	%
Barrel rear temperature	204 to 246	°C
Barrel middle temperature	204 to 246	°C
Barrel front temperature	204 to 246	°C
Nozzle temperature	216 to 260	°C
Mold temperature	60 to 93	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.