| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High Heat Resistance,Hypocrystalline,Good Tensile Strength,Solvent resistance |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.050 to 0.20 | % | ASTM D955 |
| TD | 1.5 to 1.9 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃，4 mm | 11000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃, 4 mm | 155 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃, 4 mm | 4.0 | % | ISO 527-2/5 |
| Bending modulus | 10300 | MPa | ISO 178 |
| bending strength | |||
| — | 231 | MPa | ASTM D790 |
| — | 210 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 18 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 65 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 261 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+2 to 1.0E+4 | ohms·cm | ASTM D257 |
| Electrostatic attenuation – (Mil-B-81705C), 12% RH, 5000 kV to 50 kV | 0.003 | sec |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 288 to 304 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ±0.03 |
| 3. Bergmann method |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |