| Stat-Tech™ Compound combines PP with conductive reinforcing additives.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Conductive,Antistatic property |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.80 to 1.0 | % | ASTM D955 |
| TD | 0.80 to 1.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 25.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 12 | % | ASTM D638 |
| Bending modulus | 1690 | MPa | ASTM D790 |
| bending strength | 42.4 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 320 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 3.2 mm | 98.0 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 50.0 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+3 to 1.0E+5 | ohms·cm | ASTM D257 |
| Electrostatic attenuation – (Mil-B-81705C), 12% RH, 5000 kV to 50 kV | 2 | msec | |
| Surface resistivity | 1000 to 100000 | ohms/sq | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 218 to 238 | °C | |
| Barrel middle temperature | 213 to 232 | °C | |
| Barrel front temperature | 207 to 227 | °C | |
| Nozzle temperature | 213 to 232 | °C | |
| Mold temperature | 66 to 82 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |