| About |
|---|
| STERLENE™ HMU210 is a compounded mineral filled polypropylene (TPO) for injection molding, characterised by good dimensional stability and good heat resistance, suitable for automotive underhood application.&& |
| Product Description | |
|---|---|
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 13 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 15.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| 23℃，24hr | 0.034 | % | Internal Method |
| Ash Content | |||
| 600℃ | 20 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2850 | MPa | ISO 527-2/50 |
| tensile strength | |||
| Yield, 23 ℃ | 27.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| Yield, 23 ℃ | 6.5 | % | ISO 527-2/50 |
| Fracture, 23 ℃ | 25 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2440 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 47.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, completely fractured | 4.6 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 87.0 | ℃ | ISO 75-2/Af |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 190 to 240 | °C | |
| Mold temperature | 25 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure B |
| 3. 30 min |
| 4. 0.079 in/min |
| 5. 85°C x 2hr anneal |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |