| About |
|---|
| Production-Grade Thermoplastic for Fortus 3D Production Systems ABS-M30i is a high strength material well suited for the medical, pharmaceutical and food packaging industries. Parts manufactured with ABS-M30i material are biocompatible (ISO 10993 USP Class VI) and can be gamma or EtO sterilized. When combined with Fortus® 3D Production Systems, ABS-M30i gives you biocompatible Real Parts™ with excellent mechanical properties that are well suited for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts.&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Biocompatible,High Heat Resistance,Radiation disinfection,Durability,Solvent resistance,Ethylene oxide disinfection,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Thickness（Layer Capability） | 127.0 to 330.2 | µm | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 140 | J/m | ASTM D256-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 280 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 95.6 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 82.2 | ℃ | ASTM D648 |
| Glass transition temperature | 108 | ℃ | DSC |
| Vicat Softening Temp | 98.9 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD | 8.8E-5 | 1/℃ | ASTM E831 |
| TD | 8.5E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 3.1 to 15 | kV/mm | ASTM D149 |
| Dielectric constant | 2.70 to 2.90 | ASTM D150 | |
| Dissipation factor | 5.1E-3 to 5.3E-3 | ASTM D150 | |
| Volumetric resistance | 6.0E+13 to 1.5E+14 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 110 | ASTM D785 | |
| Tensile modulus | |||
| 3.18 mm | 2410 | MPa | ASTM D638 |
| tensile strength | |||
| 3.18 mm | 35.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 4.0 | % | ASTM D638 |
| Bending modulus | 2320 | MPa | ASTM D790 |
| bending strength | 60.7 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. Method I (3 point load), 0.050 in/min |
| 4. Rate B (120°C/h), Loading 2 (50 N) |
| 5. Method A (Short-Time) |
| 6. All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |