| Production-Grade Thermoplastic for Fortus 3D Production Systems A true industrial thermoplastic, PC (polycarbonate) is widely used in automotive, aerospace, medical and many other applications. PC offers accuracy, durability and stability, creating strong parts that withstand functional testing. A PC part manufactured on a Fortus® 3D Production System is 5-60 percent stronger than a part made on previous FDM® systems. It also has superior mechanical properties to ABS and a number of other thermoplastics. When combined with a Fortus system, PC gives you Real Parts™ for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts.&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good disinfection,High Heat Resistance,Durability,Solvent resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Thickness（Layer Capability） | 127.0 to 330.2 | µm | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 320 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 138 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 127 | ℃ | ASTM D648 |
| Glass transition temperature | 161 | ℃ | DMA |
| Vicat Softening Temp | 139 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD | 6.8E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 14 to 15 | kV/mm | ASTM D149 |
| Dielectric constant | 2.80 to 3.00 | ASTM D150 | |
| Dissipation factor | 5.0E-4 to 6.0E-4 | ASTM D150 | |
| Volumetric resistance | 6.0E+13 to 2.0E+14 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| Tensile modulus | |||
| 3.18 mm | 2280 | MPa | ASTM D638 |
| tensile strength | |||
| 3.18 mm | 67.6 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 5.0 | % | ASTM D638 |
| Bending modulus | 2230 | MPa | ASTM D790 |
| bending strength | 104 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |