| Strator® C-4, a 40% long glass fiber reinforced high-flow PA66 alloy and can easily be processed on most injection molding machines.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PA66 Alloy |
| Material Status | Commercial: Negative |
| Features | High liquidity |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.30 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| 23℃ | 13000 | MPa | ISO 527-2 |
| 90℃ | 8800 | MPa | ISO 527-2 |
| 120℃ | 7800 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Fracture, 23 ℃ | 220 | MPa | ISO 527-2 |
| Fracture, 90 ℃ | 145 | MPa | ISO 527-2 |
| Fracture, 120 ℃ | 125 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.2 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 10900 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 330 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 30 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 70 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 245 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 237 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 2.3E-5 | 1/℃ | ISO 7991 |
| Thermal conductivity coefficient | 0.33 | W/m/K | ISO 22007 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | ASTM D257 |
| Dielectric strength | |||
| 2 mm | 35 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 500 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Proposed maximum recycled material ratio | 15 | % | |
| Barrel rear temperature | 270 to 300 | °C | |
| Barrel middle temperature | 270 to 300 | °C | |
| Barrel front temperature | 285 to 310 | °C | |
| Nozzle temperature | 285 to 320 | °C | |
| Processing (melt) temperature | < 310 | °C | |
| Mold temperature | 80 to 160 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with S.O.P. methods |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |