| “Stretchene” RP1903 is a random copolymer, suitable for injection stretch blow moulding (ISBM) applications. The product features very good transparency and gloss. “Stretchene” RP1903 is commonly used in packaging of detergents, cosmetics and others where ISBM bottles are used as the packaging.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,Nucleation,Food contact compliance,Random copolymer,Solvent resistance,Resistance to detergents |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 15.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0℃ | 2.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| 0℃ | 100 | kJ/m² | |
| 23℃ | 200 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 72.0 | ℃ | ISO 75-2/B |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 400 µm | < 3.0 | % | |
| 1000 µ m, injection molding | 9.0 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 58.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1100 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 30.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 14 | % | |
| fracture | > 50 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. .4 mm blown bottle wall |
| 3. 1mm disk |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |