| About |
|---|
| Styrolution PS 147F is a highly transparent GPPS grade. It gives excellent mechanical and heat resistance properties while providing with easy processability and short cycle time. FEATURES Medium Flow Easy processability Good mechanical and heat resistance properties APPLICATIONS Transparent parts for refrigerators such as fruit and vegetable crispers, chillers, flaps, trays etc Stationery products like pen barrels, scales etc. Household applications such as crystalware, kitchen containers etc. Packaging applications such as chocolate boxes, display cabinets, etc. Other transparent articles in injection Molding applications&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PS (GPPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Quick molding cycle,High Heat Resistance,Moderate liquidity |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 200℃，5 kg | 6.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.60 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | < 0.10 | % | |
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 17 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 93.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 85.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 100 | ℃ | ISO 306/A50 |
| B50 | 95.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.5 mm | 140 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 2.50 | ||
| 1 MHz | 2.50 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 150 | MPa | ISO 2039-1 |
| Tensile modulus | 3300 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| bending strength | 98.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 260 | °C | |
| Mold temperature | 10.0 to 60.0 | °C | |
| Injection Velocity | 200 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 3. Short Time |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |