| About |
|---|
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PS (HIPS) |
| Material Status | Commercial: Negative |
| Features | High impact resistance,Good Dimensional Stability,HB |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | kg/m³ | ISO 1183 |
| Melt index | |||
| 200℃，5.0kg | 3.5 | g/10min | ISO 1133 |
| 200℃，5.0kg | 3.1 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.4 – 0.7 | % | ISO 294 |
| Water absorption rate | |||
| 23 ℃, saturated | 0.06 | % | ISO 62 |
| Bulk density | |||
| Excluding external lubricants | 0.6 | kg/m³ | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 13 | KJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70 | ℃ | ISO 75 |
| 0.45 MPa, unannealed | 82 | ℃ | ISO 75 |
| Vicat Softening Temp | |||
| 50℃/hr，10N | 95 | ℃ | ISO 306 |
| 50℃/hr，50N | 83 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 9.1E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1E+13 | ohm | IEC 62631-3-1 |
| Insulation strength | |||
| 1.5 mm, short-term | 150 | kV/mm | IEC 60243 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1600 | MPa | ISO 527 |
| tensile strength | |||
| Yield, 23 ℃ | 19 | MPa | ISO 527 |
| elongation at break | 70 | % | ISO 527 |
| bending strength | |||
| 23℃ | 35 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 1600 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 70 | °C | null |
| Drying time | 2 | hr | null |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |