| Styrolux® 693D is a clear styrene-butadiene copolymer (SBC) with a well balanced combination of toughness and clarity. Styrolux 693D is mainly used for thermoformed articles, especially in blends with general-purpose polystyrene. Styrolux® 693D contains a microcrystalline wax which acts as an antiblock providing processing benefits but decreases the printability. FEATURES Good clarity Very high toughness Good GPPS blend capability APPLICATIONS Food and non-food packaging Blown film Cups for cold beverages Thermoformed transparent containers Toys&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | SBC |
| Material Status | Commercial: Active |
| Features | High anti-blocking,Block Copolymer,Ultra high toughness |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 200℃，5 kg | 12.5 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 1.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.070 | % | ISO 62 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strain | |||
| Yield, 23 ℃ | 2.2 | % | ISO 527-2 |
| MD, fracture | 260 | % | ISO 527-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179 | |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 2.5 | kJ/m² | ISO 180-A |
| 23℃ | 3.5 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 72.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 59.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 76.0 | ℃ | ISO 306/A50 |
| B50 | 48.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 to 9.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 100 Hz | 2.50 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 3.0E-4 | IEC 60250 | |
| 1 MHz | 8.0E-4 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.570 | ISO 489 | |
| Transmittance | |||
| 550 nm | 89.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ISO 868 | |
| Tensile modulus | 1300 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 22.0 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | 260 | % | ISO 527-2 |
| Bending modulus | 1400 | MPa | ISO 178 |
| bending strength | |||
| — | 32.0 | MPa | ISO 178 |
| 5% strain | 32.0 | MPa |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 250 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |