| STYRON A-TECH™ 1173 advanced technology polystyrene resin is a high impact, environmental stress crack resistant (ESCR) resin for extrusion thermoforming applications. The improved rigidity of this resin allows potential down-gauging and scrap reduction, as well as overall improvements in process efficiency. Main Characteristics: Easy processing Outstanding thermoformability Good practical toughness ESCR performance Complies with: U.S. FDA 21 CFR 177.1640 Consult the regulation for complete details. Applications: Large appliance/refrigerator liners Other deep draw extrusion thermoforming applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,High impact resistance,High ESCR,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 2.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| Yield, molding | 13.1 | MPa | ASTM D638 |
| Yield, injection molding | 17.2 | MPa | ASTM D638 |
| Fracture, molded | 15.9 | MPa | ASTM D638 |
| Fracture, injection molding | 27.6 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Fracture, molded | 30 | % | ASTM D638 |
| Fracture, injection molding | 55 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| Compression Molding | 1200 | MPa | ASTM D790 |
| injection molding | 1510 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| Compression Molding | 27.6 | MPa | ASTM D790 |
| injection molding | 40.7 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23 ℃, molded | 80 | J/m | ASTM D256 |
| 23 ℃, injection molding | 90 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed | 71.1 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 97.8 | ℃ | ASTM D648 |
| Vicat Softening Temp | 104 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |