| STYRON A-TECH™ 1200 is a newly developed, high-impact polystyrene (HIPS) resin based on patented technology. The technology platform for STYRON A-Tech makes it possible to eliminate the typical trade-offs among the key properties for HIPS including toughness, gloss, stiffness and processability. Main Characteristics: Unique combination of toughness and stiffness Ease of processing Excellent thermoforming behaviour Good blendability with General Purpose Polystyrene (GPPS) Allows for down-gauging Applications: Form Fill Seal (FFS) Pre-Forms (DFS) Vending cups Complies with: Europe REGULATION (EC) 10/2011 U.S. FDA 21 CFR 177.1640 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,High impact resistance |
| Availabilitys | Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Density | 1.05 | g/cm³ | ISO 1183-2 |
| Apparent density | 0.60 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 5.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 200℃，5 kg | 5.00 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| saturated | 0.0 | % | ISO 62-2 |
| balance | 0.10 | % | ISO 62-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1750 | MPa | ISO 527-1-2 |
| Tensile modulus | 1750 | MPa | ISO 527-2 2 |
| tensile strength | |||
| fracture | 22.0 | MPa | ISO 527-2/5 |
| yield | 19.5 | MPa | ISO 527-2/5 |
| yield | 19.0 | MPa | ISO 527-2 2 |
| Tensile strain | |||
| yield | 1.3 | % | ISO 527-2 2 |
| Nominal tensile fracture strain | 65 | % | ISO 527-2/5 |
| Nominal strain at break | > 50 | % | ISO 527-2 2 |
| Bending modulus | 1950 | MPa | ISO 178 |
| bending strength | 38.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 8.00 | kJ/m² | ISO 179/1eA 2 |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 | |
| Impact strength of cantilever beam notch | 14 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 66.0 | ℃ | ISO 75-2 2 |
| 0.45 MPa | 79.0 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | 100 | ℃ | ISO 306/A120 |
| B50 | 85.0 | ℃ | ISO 306 2 |
| Linear coefficient of thermal expansion | |||
| TD | 7.0E-5 | 1/℃ | ISO 11359-2 2 |
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |