| About |
|---|
| STYRON™ HIPS is a high clarity, high gloss polystyrene with excellent mechanical properties on thermoformed parts. Main Characteristics: High clarity Excellent gloss High heat High flow Easy processing Excellent mechanical properties of thermoformed parts Applications: Transparent Packaging Applications: Form Fill Seal (FFS), pre-forms (DFS), Disposables and Bi-Oriented Polystyrene (BOPS). Gloss cap-layer for extrusion Complies with: Europe REGULATION (EC) 10/2011 Meets Essential Req. of 94/62/EC(Packaging) U.S. FDA 21 CFR 177.1640 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good surface appearance,High liquidity,High Heat Resistance |
| Availabilitys | Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.3 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm | 2700 | MPa | ASTM D638 |
| 3.20 mm | 2700 | MPa | ISO 527-2/5 |
| tensile strength | |||
| Yield, 3.20 mm | 33.0 | MPa | ASTM D638 |
| Yield, 3.20 mm | 33.0 | MPa | ISO 527-2/5 |
| Fracture, 3.20 mm | 27.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm | 27.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 3.20 mm | > 20 | % | ASTM D638 |
| Fracture, 3.20 mm | > 20 | % | ISO 527-2/5 |
| Bending modulus | |||
| 3.20 mm | 2600 | MPa | ASTM D790 |
| 3.20 mm | 2600 | MPa | ISO 178 |
| bending strength | |||
| 3.20 mm | 62.0 | MPa | ASTM D790 |
| 3.20 mm | 62.0 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 72.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 100 | ℃ | ISO 306/A120 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, thermoplastic | 60 | ASTM D523 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Method I (3 point load), 0.051 in/min |
| 4. 0.051 in/min |
| 5. 3 point load |
| 6. Rate B (120°C/h), Loading 1 (10 N) |
| 7. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |