| STYRON X-TECH™ 2175 is an environmental stress crack resistant (ESCR) HIPS resin especially developed for thermoforming and extrusion, especially for the refrigeration industry, the production of inner liners for fridges and freezers. Based on patented Trinseo technology, this resin allows potentially 5 % down gauging of the average sheet extrusion thickness for thermoforming of the inner liners, through its unique combination of ESCR, rigidity and melt strength. Main Characteristics Allows for downgauging ESCR to food stuff and hydrocarbons Ease of processing in extrusion and thermoforming Excellent thermoforming behaviour Increased rigidity Applications Large appliances / refrigeration liners General extrusion/thermoforming applications requiring ESCR Complies with Europe Regulation (EC) 10/2011 FDA, 21 CFR 177.1640 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Food contact compliance,Good melt strength,High ESCR |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Apparent density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 2.6 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 1700 | MPa | ASTM D638 |
| — | 1700 | MPa | ISO 527-2/5 |
| tensile strength | |||
| yield | 16.0 | MPa | ASTM D638 |
| yield | 16.0 | MPa | ISO 527-2/5 |
| fracture | 26.0 | MPa | ASTM D638 |
| fracture | 26.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 63 | % | ASTM D638 |
| fracture | 63 | % | ISO 527-2/5 |
| Bending modulus | |||
| — | 1800 | MPa | ASTM D790 |
| — | 1800 | MPa | ISO 178 |
| bending strength | |||
| — | 37.0 | MPa | ASTM D790 |
| — | 37.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.6 | kJ/m² | |
| 23℃ | 9.1 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 82 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 82.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 69.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 99.0 | ℃ | ISO 306/A120 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Method I (3 point load), 0.051 in/min |
| 4. Rate B (120°C/h), Loading 1 (10 N) |
| 5. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |