| About |
|---|
| SUMIKAEXCEL® PES 3601GL30 is a Polyethersulfone (PESU) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of SUMIKAEXCEL® PES 3601GL30 are: Flame Rated Chemical Resistant Creep Resistant Flame Retardant Good Dimensional Stability&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Good Dimensional Stability,High liquidity,Flame Characteristics,High Heat Resistance,Grease resistance,Solvent resistance,Gasoline resistance,High ESCR,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.20 | % | ASTM D955 |
| TD | 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 81 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 6.4 mm | 540 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 216 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD：-50~150℃ | 2.3E-5 | 1/℃ | ASTM D696 |
| TD：50~150℃ | 4.3E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Arc resistance | 150 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.43 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 134 | ASTM D785 | |
| tensile strength | 140 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 8400 | MPa | ASTM D790 |
| bending strength | 190 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 310 to 340 | °C | |
| Barrel middle temperature | 340 to 380 | °C | |
| Barrel front temperature | 340 to 380 | °C | |
| Nozzle temperature | 340 to 380 | °C | |
| Processing (melt) temperature | 350 to 360 | °C | |
| Mold temperature | 120 to 160 | °C | |
| Injection pressure | 118 to 157 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |