| About |
|---|
| SUMIKAEXCEL® PES 4101GL30是一种聚醚砜(PES)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在亚太地区、北美洲或欧洲有供货,加工方式为:注射成型。 SUMIKAEXCEL® PES 4101GL30的主要特性有: 阻燃/额定火焰 耐化学品 Flame Retardant 抗蠕变 耐冲击&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Grease resistance,Solvent resistance,Gasoline resistance,High ESCR,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.20 | % | ASTM D955 |
| TD | 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 81 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 6.4 mm | 540 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 216 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD：-50~150℃ | 2.3E-5 | 1/℃ | ASTM D696 |
| TD：50~150℃ | 4.3E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Arc resistance | 150 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.43 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 134 | ASTM D785 | |
| tensile strength | 140 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 8400 | MPa | ASTM D790 |
| bending strength | 190 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 310 to 340 | °C | |
| Barrel middle temperature | 340 to 380 | °C | |
| Barrel front temperature | 340 to 380 | °C | |
| Nozzle temperature | 340 to 380 | °C | |
| Processing (melt) temperature | 350 to 360 | °C | |
| Mold temperature | 120 to 160 | °C | |
| Injection pressure | 118 to 157 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |