| SUMIKON® AM-100 type J black-B is a short glass fiber reinforced, non-flame retardant, diallyl phthalate molding compound.&& |
| Product Description | |
|---|---|
| Supplier | SBHPP |
| Generic | DAP增塑剂 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.66 | g/cm³ | JIS K6911 |
| Shrinkage rate | |||
| MD | 0.52 | % | JIS K6911 |
| Water absorption rate | |||
| by boiling | 0.19 | % | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 10300 | MPa | JIS K6911 |
| bending strength | 135 | MPa | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.2 | kJ/m² | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 224 | ℃ | JIS K6911 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 13 | kV/mm | JIS K6911 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| insulation resistance | JIS K6911 | ||
| — | 1.0E+15 | ohms | JIS K6911 |
| — | 2.0E+14 | ohms | JIS K6911 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.69 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B (Step-by-Step) |
| 3. After boiling |
| 4. As molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |