| Durez “SUMIKON” PM-9610 black Phenolic is a two stage glass and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and higher dimensional stability with excellent heat resistance. Typical applications include brush holders for high temperature, and timing pulleys.&& |
| Product Description | |
|---|---|
| Supplier | SBHPP |
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Halogen free,High Heat Resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.02 | g/cm³ | ASTM D792 |
| Apparent density | 0.96 | g/cm³ | ASTM D1895 |
| Shrinkage rate | |||
| MD | 0.25 | % | ASTM D6289 |
| Water absorption rate | |||
| balance | 0.030 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 24800 | MPa | ASTM D638 |
| tensile strength | 96.0 | MPa | ASTM D638 |
| bending strength | 172 | MPa | ASTM D790 |
| compressive strength | 241 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 21 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 210 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| — | 15 | kV/mm | ASTM D149 |
| — | 9.8 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 4.90 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.030 | ASTM D150 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 3. Method B (Step-by-Step) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |