| About |
|---|
| SUMIKON® PM-9630 (Type JT Black) is Glass fiber and Inorganic filler filled resol resin (non-anmonia phenolic) molding compound with good electronic property and heat resistance. This grade is official registered UL with V-0 (t=0.16).&& |
| Product Description | |
|---|---|
| Supplier | SBHPP |
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Heat Resistance, Good,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.77 | g/cm³ | JIS K6911 |
| Shrinkage rate | |||
| MD | 0.16 | % | JIS K6911 |
| Water absorption rate | |||
| balance | 0.090 | % | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 137 | MPa | JIS K6911 |
| Bending modulus | 14600 | MPa | JIS K6911 |
| bending strength | 208 | MPa | JIS K6911 |
| compressive strength | 208 | MPa | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.4 | kJ/m² | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 300 | ℃ | JIS K6911 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 9.0 | kV/mm | JIS K6911 |
| Arc resistance | 179 | sec | JIS K6911 |
| insulation resistance | JIS K6911 | ||
| — | 4.0E+12 | ohms | JIS K6911 |
| — | 1.0E+12 | ohms | JIS K6911 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.160 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B (Step-by-Step) |
| 3. After boiling |
| 4. As molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |