| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Material Status | Commercial: Negative |
| Features | High Heat Resistance,Good liquidity,Optical performance,HB |
| Availabilitys | Asia Pacific,Europe,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | JIS K7112 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 2.0 | g/10min | JIS K7210 |
| Shrinkage rate | |||
| MD | 0.20 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | JIS K7209 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.3 | kJ/m² | JIS K7110 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 96.0 | ℃ | JIS K7207 |
| Vicat Softening Temp | 106 | ℃ | JIS K7206 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+16 | ohms | JIS K6911 |
| Volume resistivity | > 1.0E+15 | ohms·cm | JIS K6911 |
| Dielectric constant | 3.10 | JIS K6911 | |
| Dissipation factor | 0.040 | JIS K6911 | |
| insulation resistance | > 1.0E+15 | ohms | JIS K6911 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm, all colors | HB | UL 94 | |
| Burning rate | 30 | mm/min | ASTM D63 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | JIS K7105 | |
| Transmittance | 93.0 | % | JIS K7105 |
| Haze | < 0.50 | % | JIS K7105 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Voltage Resistance | 20.0 | kV/min | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 63.0 | MPa | JIS K7113 |
| Tensile strain | |||
| fracture | 5.0 | % | JIS K7113 |
| Bending modulus | 3200 | MPa | JIS K7203 |
| bending strength | 94.0 | MPa | JIS K7203 |
| Bending stiffness | 4.0 | % | JIS K7203 |
| Rockwell hardness | |||
| M-level | 95 | JIS K7202 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 70 to 80 | °C | null |
| Drying time | 4.0 to 6.0 | hr | null |
| Temperature at the rear of the barrel | 200 to 260 | °C | null |
| Temperature in the middle of the barrel | 200 to 260 | °C | null |
| Front temperature of material barrel | 200 to 260 | °C | null |
| Mold temperature | 60 to 80 | °C | null |
| Injection pressure | 58.8 to 118 | MPa | null |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |