| Applications: For shopping and grocery bags, perforated rolls, trash bags, and industrial liners. Characteristics: Bimodal blown film grade having high tensile and impact strength, good stiffness and barrier properties with a wide molecular weight distribution for easy processing. Performs well under heavy load conditions.&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Wide molecular weight distribution,Good Tensile Strength,Block resin |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ASTM D792-A |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.050 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 9.3 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus -1% secant, MD | ASTM D882 | ||
| — | 990 | MPa | ASTM D882 |
| — | 930 | MPa | ASTM D882 |
| Secant modulus -1% secant, TD | ASTM D882 | ||
| — | 1140 | MPa | ASTM D882 |
| — | 1030 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield | 35.0 | MPa | ASTM D882 |
| MD, yield | 35.0 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| TD, yield | 30.0 | MPa | ASTM D882 |
| TD, yield | 30.0 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, fracture | 75.0 | MPa | ASTM D882 |
| MD, fracture | 70.0 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| TD, fracture | 55.0 | MPa | ASTM D882 |
| TD, fracture | 65.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 520 | % | ASTM D882 |
| MD, fracture | 560 | % | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| TD, fracture | 560 | % | ASTM D882 |
| TD, fracture | 550 | % | ASTM D882 |
| Drop hammer impact | ASTM D1709 | ||
| — | 250 | g | ASTM D1709 |
| — | 330 | g | ASTM D1709 |
| Elmandorf Tear Strength – MD | ASTM D1922 | ||
| — | 11 | g | ASTM D1922 |
| — | 17 | g | ASTM D1922 |
| tear strength | ASTM D1922 | ||
| TD | 78 | g | ASTM D1922 |
| TD | 39 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 4 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. With stabilizer |
| 3. Without stabilizer |
| 4. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |