| About |
|---|
| Supering RP 525 – GMP is a Polytetrafluoroethylene (PTFE) product. It can be processed by injection molding or sintering and is available in Latin America or North America.&& |
| Product Description | |
|---|---|
| Generic | PTFE |
| Material Status | Commercial: Active |
| Features | Good liquidity |
| Availabilitys | North America,Latin America |
| Process Methods | sintering |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.99 to 2.04 | g/cm³ | Internal Method |
| Apparent density | 0.50 to 0.60 | g/cm³ | Internal Method |
| Particle size distribution | |||
| d50 | 453.0 to 713.0 | µm | Internal Method |
| Shrinkage rate | |||
| Sintering | 0.50 to 1.5 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 61 to 67 | Internal Method |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 12.0 | MPa | Internal Method |
| Tensile strain | |||
| fracture | 70 | % | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| sintering temperature | |||
| Maximum | 360 | ℃ | |
| Flow time | |||
| 50 grams | 2.9 to 4.5 | sec | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Mold temperature | 21 to 25 | °C | |
| Injection pressure | 63.7 to 73.5 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |