Supol H-622 - SOLIAO

About
H-622 by reactive extrusion into the legal system of maleic anhydride grafted elastomer copolymer of ethylene and octene copolymer ( POE ) , substrate selection . H-622 has a low gel, grafting ratio, light in color, which is widely used in engineering plastics ( PA6 , PA66 , PBT , etc.) of toughening modification; also can be used as a compatibilizer to improve the glass fiber, fillers and the compatibility of the matrix resin; and greatly improve the adhesion between the resin or resin metal in the multi-layer co-extruded. Typical applications PA6 , PA66 , PBT , and other engineering plastics flexibilizer of glass fiber reinforced and fill the PA of PBT do compatibilizer to improve the interface compatibility performance PA / PP alloy compatibility agent Bond performance of the multi-layer co-extruded film resin layer between the resin between the metal&&

About

H-622 by reactive extrusion into the legal system of maleic anhydride grafted elastomer copolymer of ethylene and octene copolymer ( POE ) , substrate selection . H-622 has a low gel, grafting ratio, light in color, which is widely used in engineering plastics ( PA6 , PA66 , PBT , etc.) of toughening modification; also can be used as a compatibilizer to improve the glass fiber, fillers and the compatibility of the matrix resin; and greatly improve the adhesion between the resin or resin metal in the multi-layer co-extruded. Typical applications PA6 , PA66 , PBT , and other engineering plastics flexibilizer of glass fiber reinforced and fill the PA of PBT do compatibilizer to improve the interface compatibility performance PA / PP alloy compatibility agent Bond performance of the multi-layer co-extruded film resin layer between the resin between the metal&&

Product Description
Supplier	LyondellBasell
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	Low speed solidification point,Good bond,Octene copolymer,Copolymer
Availabilitys	Asia Pacific
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.880	g/cm³	ASTM D792
Melt Flow Rate
230℃，10.0kg	1.0	g/10min	ASTM D1238
MAH grafting level	Gao

MECHANICAL	Nominal value	Unit	Test method
Shore hardness	80		ASTM D2240
tensile strength	8.00	MPa	ASTM D638
Tensile strain
fracture	400	%	ASTM D638
Bending modulus	155	MPa	ASTM D790A

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.