| About |
|---|
| SUPREME Specialty PS SP255是一种专用型聚苯乙烯产品,。 它可以通过挤出、注射成型或热成型进行加工,在亚太地区、北美洲、欧洲或非洲和中东有供货。 SUPREME Specialty PS SP255的应用领域包括医疗/保健、容器、薄板 和 食品接触应用。 特性包括: 阻燃/额定火焰 良好的柔韧性 良好的韧性 透明度 高强度&& |
| Product Description | |
|---|---|
| Generic | PS (special type) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good flexibility,High liquidity,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23 ℃, 3.20 mm, injection molding | 400 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.20 mm, injection molding | 10 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, 3.20 mm, injection molding | 22000 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, 3.20 mm, injection molding | 550 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm, injection molded | 77.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 1000 µm | 88.0 | % | ASTM D1003 |
| Haze | |||
| 1000 µ m, injection molding | 2.5 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | < 220 | °C | |
| Mold temperature | 40 to 50 | °C | |
| Melt temperature | < 220 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |