| SUPREME Specialty PS SP6530是一种专用型聚苯乙烯产品,。 它,在亚太地区、北美洲、欧洲或非洲和中东有供货。 SUPREME Specialty PS SP6530的应用领域包括商业/办公用品 和 房屋。 主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Generic | PS (special type) |
| Material Status | Commercial: Active |
| Features | Antistatic property,Good coloring,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 18 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23 ℃, 3.20 mm, injection molding | 22.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.20 mm, injection molding | 40 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, 3.20 mm, injection molding | 1950 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, 3.20 mm, injection molding | 40.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 70 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm, injection molded | 71.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 89.0 | ℃ | ASTM D1525 3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume resistivity | |||
| 23 ℃，3.20 mm | 1.0E+14 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | < 230 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 | hr | |
| Melt temperature | < 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |