| HS-030 is a certified prime resin designed for extrusion-thermoforming applications requiring good rigidity and elongation. The low residual volatiles of this resin makes it particularly suitable for packaging taste and odor sensitive articles. HS-030 is a medium-flow grade that offers excellent melt uniformity and consistency of flow, superior impact resistance and very good extrusion and thermoform processability. HS-030 complies with FDA regulation 21CFR 177.1640, and with most international regulations concerning the use of Polystyrene in contact with food articles.&& |
| Product Description | |
|---|---|
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Low Residuals,Good liquidity,Food contact compliance,Low odor,Good Tensile Strength |
| Availabilitys | North America |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm, injection molded | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 93.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 55 | ASTM D785 | |
| Tensile modulus | 2200 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 24.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 45 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 2280 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |