| About |
|---|
| LD20-008 is a certified prime resin specially designed for production of shrink wrapping Blown films for case bundling applications requiring excellent shrink performance, very high toughness, good puncture and burn-through resistance. LD20-008 is also recommended for impact liner films. It features easy processability with excellent film optical and mechanical properties. Minimum recommended film thickness is 1.5 mils. LD20-008 contains no slip and no antiblock.&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Optical performance,Ultra high toughness,Low density,Puncture Resistant,High shrinkage |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 38 µ m | 186 | MPa | ASTM D882 |
| 1% secant, TD: 38 µ m | 235 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 38 µ m | 12.0 | MPa | ASTM D882 |
| TD, yield, 38 µ m | 12.0 | MPa | ASTM D882 |
| MD, fracture, 38 µ m | 31.0 | MPa | ASTM D882 |
| TD, fracture, 38 µ m | 23.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 38 µ m | 220 | % | ASTM D882 |
| TD, fracture, 38 µ m | 550 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µm | 95 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：38 µm | 720 | g | ASTM D1922 |
| TD：38 µm | 140 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 60 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 6.8 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |