Surlyn® E185SB

About
DuPont™ Surlyn® E185SB is an ionomer of ethylene acid acrylate terpolymer. The resin can be processed in conventional blown film, cast film, sheet extrusion and coextrusion equipment designed to process polyethylene and ethylene copolymer type resins. Surlyn® E185SB can be coextruded with HDPE to provide delamination-type peelable seals. The seal strength can be controlled by processing conditions and/or the thickness of Surlyn® E185SB layer. Thickness is typically in the range of 5 to 15 microns (0.20 to 0.60 mils). Other benefits of Surlyn® E185SB include: Very low seal initiation temperature Broad sealing temperature range&&

About

DuPont™ Surlyn® E185SB is an ionomer of ethylene acid acrylate terpolymer. The resin can be processed in conventional blown film, cast film, sheet extrusion and coextrusion equipment designed to process polyethylene and ethylene copolymer type resins. Surlyn® E185SB can be coextruded with HDPE to provide delamination-type peelable seals. The seal strength can be controlled by processing conditions and/or the thickness of Surlyn® E185SB layer. Thickness is typically in the range of 5 to 15 microns (0.20 to 0.60 mils). Other benefits of Surlyn® E185SB include: Very low seal initiation temperature Broad sealing temperature range&&

Product Description
Supplier	DOW
Generic	离聚物
Material Status	Commercial: Active
Features	Smoothness,High anti-blocking,Food contact compliance,Low temperature heat sealing
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.950	g/cm³	ASTM D792
Density	0.950	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.0	g/10min	ASTM D1238
190℃，2.16kg	3.0	g/10min	ISO 1133

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	60.0	℃	ASTM D1525
Vicat Softening Temp	60.0	℃	ISO 306
Melting peak temperature	89.0	℃	ASTM D3417
Melting temperature
DSC	89.0	℃	ISO 3146
freezing point
—	62	℃	ISO 3146
—	62	℃	ASTM D3417

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	135	°C
Barrel 2 zone temperature	160	°C
Barrel 3 zone temperature	185	°C
Barrel 4 zone temperature	185	°C
Barrel 5 zone temperature	185	°C
Connector temperature	185	°C
Melt temperature	160 to 235	°C
Nozzle temperature	185	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.