| About |
|---|
| SURPASS® FPs016-C is a Linear Low Density Polyethylene material. It is available in North America for film extrusion. Important attributes of SURPASS® FPs016-C are: Antioxidant Food Contact Acceptable Good Tear Strength Good Toughness Octene Comonomer Typical applications include: Coating Applications Film Food Contact Applications&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low speed solidification point,Food contact compliance,Inoxidizability,Good melt strength,Low density,Good tear strength,Octene copolymer |
| Availabilitys | North America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.916 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.65 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| 1% secant, TD, 25 µ m, blow molded film | 138 | MPa | ASTM D882 |
| 1% secant, MD, 25 µ m, blow molded film | 126 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 44.0 | MPa | ASTM D882 |
| TD, yield, 25 µ m, blow molded film | 8.50 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 47.0 | MPa | ASTM D882 |
| MD, yield, 25 µ m, blow molded film | 8.50 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 780 | % | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 470 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 700 | g | ASTM D1709-A |
| tear strength | |||
| TD, 25 µ m, blow molded film | 430 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 350 | g | ASTM D1922 |
| Sealing starting temperature | |||
| 25 µ m, blow molded film | 100 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 45 °, 25 µ m, blow molded film | 72 | ASTM D2457 | |
| 45 °, 25 µ m, blow molded film | 38 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25 µ m, blow molded film | 7.0 | % | ASTM D1003 |
| 25 µ m, blow molded film | 15 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Low friction puncture | |||
| Blow molded film, 25.0 µ m | 980 | J/cm |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Temperature at which a 2 mil film achieves a seal strength of 4.4N/13mm. 0.5 sec dwell, 0.27 N/mm² bar pressure, 305 mm/min pull speed |
| 3. LDPE Blended |
| 4. 100% LLDPE |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |