| About |
|---|
| SURPASS® FPs317-A is a Linear Low Density Polyethylene material. It is available in North America for coextrusion or film extrusion. Important attributes of SURPASS® FPs317-A are: Antioxidant Food Contact Acceptable Good Aesthetics Good Tear Strength Octene Comonomer Typical applications include: Coating Applications Film Food Contact Applications Wrap&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Optical performance,Low speed solidification point,Food contact compliance,Inoxidizability,Low density,Good tear strength,Octene copolymer,Puncture Resistant |
| Availabilitys | North America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.917 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Secant modulus | |||
| 1% secant, TD, 20 µ m, cast thin film | 120 | MPa | ASTM D882 |
| 1% secant, MD, 20 µ m, cast thin film | 100 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 20 µ m, blow molded film | 25.0 | MPa | ASTM D882 |
| TD, yield, 20 µ m, blow molded film | 7.00 | MPa | ASTM D882 |
| MD, fracture, 20 µ m, blow molded film | 32.0 | MPa | ASTM D882 |
| MD, yield, 20 µ m, blow molded film | 7.50 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 20 µ m, cast thin film | 780 | % | ASTM D882 |
| MD, fracture, 20 µ m, cast thin film | 470 | % | ASTM D882 |
| tear strength | |||
| TD, 20 µ m, cast thin film | 540 | g | ASTM D1922 |
| MD, 20 µ m, cast thin film | 380 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 20 µ m, cast thin film | 85 | ASTM D2457 | |
| Haze | |||
| 20.0 µ m, cast thin film | 0.80 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Low friction puncture | |||
| Cast thin film, 20.0 µ m | 830 | J/cm | Internal Method |
| Tensile strain | |||
| Fracture, cast film, 20 µ m | 360 | % | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |