| About |
|---|
| Product Description | |
|---|---|
| Supplier | TOSOH |
| Material Status | Commercial: Negative |
| Features | Lubricating |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Hot deformation temperature | |||
| 0.45 MPa | 190 | ℃ | ISO 75 |
| 1.8 MPa | 110 | ℃ | ISO 75 |
| TD | 5.8 | ISO 11359 | |
| MD | 5.5 | ISO 11359 | |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Flow Rate | 90 | g/10min | ISO 1133 |
| Rod flow length (1mmt) | 320 | mm | |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Water absorption rate | 0.02 | % | ISO 62 |
| Shrinkage rate | |||
| TD | 1.4 | % | |
| MD | 1.2 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 30 | MPa | ISO 527 |
| tensile strength | |||
| yield | 35 | MPa | ASTM 638 |
| Tensile strain | |||
| fracture | 1.2 | % | ISO 527 |
| bending strength | 70 | MPa | ISO 178 |
| Bending modulus | 3000 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 111 | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | 1 | kJ/m² | ISO 179-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| breakdown | 17 | kV/mm | IEC 60243 |
| Arc resistance | 35 | sec | ASTM D495 |
| Dielectric constant | |||
| 1 MHz | 2.8 | IEC 60250 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |