| About |
|---|
| TAFMER™ DF610, ethylene based polymer, is a specialty olefinic resin designed to improve impact resistance flexibility and softness of Polyethylene (PE) and Polypropylene (PP).&& |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Negative |
| Features | Good Clarity,Good flexibility,High impact resistance,Crosslinked,High elastic,Foaming performance,Low density,Soft,low-temperature impact resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.862 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 1.2 | g/10min | ASTM D1238 |
| 230℃，2.16kg | 2.2 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Melting temperature | < 50.0 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 57 | ASTM D2240 | |
| tensile strength | |||
| fracture | > 3.00 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 1000 | % | ASTM D638 |
| Torsional Rigidity | 2.00 | MPa | ASTM D1043 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |